As of late 2012, the silicon standard component was changed to SRM 640d, | As of late 2012, the silicon standard component was changed to SRM 640d, | ||
for which the parameters are | for which the parameters are | ||
Space Group: F d -3 m | Space Group: F d -3 m | ||
Lattice: 5.431230 5.431230 5.431230 90.0000 90.0000 90.0000 | Lattice: 5.431230 5.431230 5.431230 90.0000 90.0000 90.0000 | ||
Atom1: Si @ x = 1/8, y = 1/8, z = 1/8 | Atom1: Si @ x = 1/8, y = 1/8, z = 1/8 | ||
Revision as of 22:41, 14 February 2013
Calibration of the wavelength at 11-BM is performed using a mixture of NIST standard reference materials (SRMs).
As of 2011, the calibration sample is a mixture of ~ 70 wt% Si (SRM 640d) and ~ 30 wt% Al2O3 (SRM 676).
Lattice & Atomic Position Values are as follows:
Si (SRM 640d) Space Group: F d -3 m Lattice: 5.431590 5.431590 5.431590 90.0000 90.0000 90.0000 Atom1: Si @ x = 1/8, y = 1/8, z = 1/8
Al2O3 (SRM 676a) Space Group: R -3 c Lattice: 4.7590914 4.7590914 12.991779 90.0000 90.0000 120.0000 Atom1: Al @ x = 0, y = 0, z = 0.351869 Atom2: O @ x = 0.307804, y = 0, z = 1/4
As of late 2012, the silicon standard component was changed to SRM 640d, for which the parameters are
Space Group: F d -3 m Lattice: 5.431230 5.431230 5.431230 90.0000 90.0000 90.0000 Atom1: Si @ x = 1/8, y = 1/8, z = 1/8